Harris® 0

Harris 0 is a low cost alloy that is suitable for most copper-to-copper or brass joints where close tolerance can be maintained.

Features

• Economical choice for copper brazing
• Copper is self-fluxing
• Alloy flows quickly at brazing temperature so requires close joint tolerance (less than 0.005")
• Primarily used in manual brazing applications
• Also a suitable for brazing brass
• Operators should avoid over heating the brass and use Stay Silv® white brazing flux
• Not recommended for brazing steel or other ferrous base metals
• Should not use Harris 0 if braze is exposed to sulfur or sulfur compounds in service
• Recommended joint clearance of .002"-.007"
• Conforms to the EU Reach & RoHS directive

Typical Applications

• Copper-to-copper joint brazing
  
• Brass joint brazing

Technical Specs

• Solidus 1310ºF (710°C)
• Liquidus 1460°F (793°C)
• Brazing Range 1345°F- 1500°F (730°C -816°C)
• AWS A5.8 BCuP-2
• ASME Section IIC SFA 5.8 BCuP-2
• ISO 17672 CuP 181

Download Tech Sheet

Options:

• .050" x 1/8" Flat Stick - 1 Tube - 5620F1
  
• 1/8" x 20" Rod - 25lb Box - 0620R
• 3/32" x 24 Stick Tube - 0520R1
• Other diameters and package sizes available upon request